特 性
Properties
|
試驗方法
Test
Methods |
實驗狀況
Test
Conditions |
單 位
Units |
通用級
General Purpose |
高流動
耐化學級
High Flow &
Chemical
Resistance |
| EN-611N |
EN-612E |
EN-612N |
EN-612HF |
衝擊強度
Izod Impact Strength
Notched |
1/4"
bar |
ASTM
D-256
Method A
|
23℃
(73℉) |
Kg-cm/cm
J/M
ft-1bs/in. |
3.8
0.7 |
3.8
0.7 |
3.8
0.7 |
2.8
0.52 |
1/8"
bar |
ASTM
D-256
Method A
|
23℃
(73℉) |
Kg-cm/cm
J/M
ft-1bs/in. |
4.0
0.74 |
4.0
0.74 |
4.0
0.74 |
3.0
0.55 |
抗張強度
Tensile Strength At
Yield Type 1, 1/8" Thickness |
ASTM
D-638
50 mm/min
|
23℃
(73℉) |
Kgf/cm2
MPa
psix103 |
700 |
700 |
730 |
530 |
抗折強度
Flexural Strength
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉) |
Kgf/cm2
MPa
psix103 |
|
|
|
|
抗折模數
Flexural Modulus
1/8"×1"×4" bar |
ASTM
D-790
15 mm/min
|
23℃
(73℉) |
Kgf/cm2
GPa
psix105 |
|
|
|
|
洛式硬度
Rockwell Hardness |
ASTM
D-785
|
23℃
(73℉) |
M Scale |
84 |
84 |
84 |
84 |
熱變形溫度(Unannealed)
Heat Deflection Temperature
1/2"×1/2"×5" bar |
ASTM
D-648 |
18.6 Kgf/cm2
(264 psi) |
℃
℉ |
92
|
92
|
92
|
90
|
熱軟化點溫度
Vicat Softening Temperature |
ASTM
D-1525
|
Load
1 Kg |
℃
℉ |
105 |
105 |
105 |
104 |
融流指數
Melting Flow Index |
ASTM
D-1238
|
200℃
5 Kg |
g/10min. |
2.2 |
3 |
4 |
11.5 |
比重
Specific Gravity |
ASTM
D-792
|
23℃
(73℉) |
--- |
|
|
|
|
UL燃燒等級
UL Flame Class Rating
(File No. E120595) |
UL 94
|
|
1/8"
Thickness |
HB |
HB |
HB |
HB |
1/16"
Thickness |
|
|
|
|
成型收縮率
Mold Shrinkage Rate |
ASTM
D-955
|
|
% |
|
|
|
|